Simulation of hydrogen and coal gas fueled flat-tubular solid oxide fuel cell (FT-SOFC)

Solid oxide fuel cells (SOFCs) are considered an important technology in terms of high efficiency and clean energy generation. Flat-tubular solid oxide fuel cell (FT-SOFC) which is a combination of tubular and planar cell geometries stands out with its performance values and low costs. In this study, the performance of an FT-SOFC is analyzed numerically by using finite element method-based design as a result of changing parameters by using different fuels which are pure hydrogen and coal gas with various proportions of CO. In addition, cell performance values for different temperatures were analyzed and interpreted. Analyzes have been performed by using COMSOL Multiphysics software. The rates of CO composition used are 10%, 20%, and 40%, respectively. In addition, the air was used as the oxidizer in all cases. The cell voltage and average cell power of the FT-SOFC were examined under the 800 °C operating condition. The maximum power value and current density value were obtained as 710 W/m² and 1420 A/m² for the flat-tubular cell, respectively. As a result of the study, it was observed that the maximum cell power densities increased with increasing temperature. Analysis results showed that FT-SOFCs have suitable properties for different fuel usage and different operating temperatures. High-performance values and design features in different operating conditions are expected to make FT-SOFC the focus of many studies in the future.     

Sintering behavior of BaCe0.7Zr0.1Y0.2O3-δ electrolyte at 1150 °C with the utilization of CuO and Bi2O3 as sintering aids and its electrical performance

BaCe_0.7Zr_0.1Y_0.2O_3-δ (BCZY) is one of the promising electrolytic candidate for solid oxide fuel cell (SOFC) due to its good proton conductivity and better stability. Herein, the effect of dual sintering aids such as CuO-Bi₂O₃ upon the sinterability at low temperature, improved electrochemical properties, and thermo-chemical changes about proton-conducting BaCe_0.7Zr_0.1Y_0.2O_3-δ electrolyte were investigated in detail. FESEM micrographs and shrinkage curves revealed significant improvement in sinterability and densifications of BCZY electrolyte. The dense pellets were sintered with CuO-Bi₂O₃ (2–3 mol %) as sintering aids at a temperature of 1150 °C for 5 h. The perfectly uniform distribution of sintering aids increased the linear shrinkage of BCZY from 5% till 19–21%. The crystallite size and grain growth within the structure was enhanced due to the formation of the melting phase of Bi₂O₃ and Cu²⁺ incorporation in the perovskite structure. The elevated and improved electrochemical measurement for BCZY with 2 mol% of CuO-Bi₂O₃ as sintering aid categorized it well suited for solid oxide fuel cells.     

Synthesis and performance evaluation of a new drag reducer based on acrylamide/12-allyloxydodecyl acid sodium

Hydraulic fracturing with slickwater is a field-proven stimulation technology used in tight reservoirs. Because of the high pumping rate associated with slickwater fracturing, drag reduction (DR) is critical in minimizing pressure drop and the success of oilfield operations. In this paper, a new type of drag reducer (SPR) was synthesized with acrylamide and 12-allyloxydodecyl acid sodium, and its drag reduction performance was evaluated. The results showed that the new drag reducer features low molecular weight, fast-dissolving rate and low interfacial tension. The algorithm of estimating the drag reduction rate of non-Newtonian fluid SPR was proposed and validated. Empirical or semianalytical models for estimating the friction ratio (σ) or friction factor (λ or f) were used to simulate the turbulence behavior of the SPR drag reducer under different Reynolds numbers (Re). The modified Virk's correlation could accurately model the turbulent behavior of the SPR drag reducer. A unified calculation formula was established in this study for different pipe diameters.     

Unipolar plasma electrolytic oxidation: Waveform optimisation for corrosion resistance of commercially pure titanium

This study deals with the anodisation of titanium grade 2 in 0.5-M sulphuric acid using a pulsed signal in a unipolar regime. The electrical parameters investigated are voltage, frequency and duty cycle. The use of duty cycles with a high percentage of anodic polarisation (90%), combined with high frequencies (1000 Hz) and the higher voltage tested (220 V), favoured the establishment of a plasma regime involving strong dielectric discharges, allowing the growth of thicker oxides but with rough architecture. The corrosion resistance of the formed film has been characterised by potentiodynamic tests in 0.5-M NaBr for localised corrosion resistance and by immersion tests in 10% v/v sulphuric acid solution for a uniform corrosion assessment. Current–time curves, visual observations and electron microscope analysis (scanning electron microscopy, energy-dispersive X-ray spectroscopy) were the tools selected to provide a correlation between technological parameters and oxide growth mechanism. For localised and uniform corrosion, anodisation at 220 V with a high level of anodic polarisation (90%) and frequency (1000 Hz) was verified to be particularly advantageous.     

Modulation of electrical transport in calcium cobaltite ceramics and thick films through microstructure control and doping

Ca₃Co₄O₉ is a promising p-type thermoelectric oxide material having intrinsically low thermal conductivity. With low cost and opportunities for automatic large scale production, thick film technologies offer considerable potential for a new generation of micro-sized thermoelectric coolers or generators. Here, based on the chemical composition optimized by traditional solid state reaction for bulk samples, we present a viable approach to modulating the electrical transport properties of screen-printed calcium cobaltite thick films through control of the microstructural evolution by optimized heat-treatment. XRD and TEM analysis confirmed the formation of high-quality calcium cobaltite grains. By creating 2.0 at% cobalt deficiency in Ca_2.7Bi_0.3Co₄O_9+δ, the pressureless sintered ceramics reached the highest power factor of 98.0 μWm^?1 K^-2 at 823 K, through enhancement of electrical conductivity by reduction of poorly conducting secondary phases. Subsequently, textured thick films of Ca_2.7Bi_0.3Co_3.92O_9+δ were efficiently tailored by controlling the sintering temperature and holding time. Optimized Ca_2.7Bi_0.3Co_3.92O_9+δ thick films sintered at 1203 K for 8 h exhibited the maximum power factor of 55.5 μWm^?1 K^-2 at 673 K through microstructure control.     

菌酶协同改善花生粕的饲用品质

花生粕是重要的蛋白饲料原料，但由于其氨基酸不平衡，特别是精氨酸与赖氨酸比例严重失衡（精氨酸与赖氨酸含量比值在3~4，理想的精氨酸与赖氨酸含量比值为1.0），限制了其在动物养殖中的应用。研究了复合酶预处理结合乳酸菌发酵花生粕对其品质的改善。结果表明：经菌酶协同处理后，花生粕粗蛋白质含量由46.4%提高至506%，大分子蛋白明显降解为小分子蛋白，酸溶蛋白质含量由2.3%提高至17.8%，多肽含量由1.6%提高至15.7%，蛋氨酸和赖氨酸含量分别提高了77.1%和42.0%，精氨酸降解率为18.7%，精氨酸与赖氨酸含量比值从3.7降低至2.1，总酸含量由06%提高到4.7%，其中乳酸含量由0.64 mg/g提高至14.63 mg/g。菌酶协同处理后的花生粕抗氧化性明显增强，其中每克菌酶协同处理后的花生粕对羟自由基的清除能力与171.6 mg VC相当，比花生粕（与47.6 mg VC相当）提高了2.6倍。     

Understanding δ-Bi2O3 fluorite degradation mechanism and related solutions for promising applications in distributed multigeneration

Oxygen selective membrane on the base of cermet δ-Bi₂O₃/Ag with an interpenetrating structure has the maximum potential efficiency of air separation. However, the degradation processes, including the phase degradation of fluorite δ-Bi₂O₃, do not make it possible to create a membrane with the required perfection and durability. In this work, the ordering of oxygen vacancies with the transformation of fluorite into the rhombohedral phase (S.G. R-3) was studied by powder HT XRD in situ at 600 °C on dense Bi_0.78Er_0.2Hf_0.02O_1.51 ceramics. Fast regeneration of disordered fluorite occurs at T = 640–700 °C. The phase degradation of fluorite due to the segregation of dopants at the second stage leads into stable phases - sillenite, tetragonal or rhombohedral phase (S.G. R-3m), depending on the composition of δ-Bi₂O₃. Fast regeneration of fluorite occurs when heated to 820 °C, which is unacceptable for membranes. Analysis of all available data allows us to propose approaches to optimize the composition of δ-Bi₂O₃ and technical solutions for creating durable oxygen selective membranes with promising use in distributed multigeneration. As a result of the analysis, a new solid electrolyte with better parameters was obtained.